Sectorial honeycomb ceramic (used as catalyst carriers,heat transfer media, filtering materials)

Sectorial honeycomb ceramic (used as catalyst carriers,heat transfer media, filtering materials) - details see: https://www.machineto.com/sectorial-honeycomb-ceramic-used-as-catalyst-carriers-heat-transfer-media-filtering-materials-10214406

Place of Origin:Jiangxi China (Mainland)	Brand Name:zhongtian	Model Number:Model	shape:monolith sectorial
material:Mullite, Cordierite ceramics and zircon chrome corundum	function:catalyst carriers,heat transfer media, filtering materials

PXZT Sectorial honeycomb ceramic

(used as catalyst carriers,heat transfer media, filtering materials)

with competitive price is your best choice.

1. Materials

Mullite, Cordierite ceramics and zircon chrome corundum, etc.

2.Application

1)As support of catalyst, ceramic honeycomb materials are typically used for purifying automotive emission, removing bad smell etc.

2) As heat exchange media, ceramic honeycomb materials are mainly utilized in heat recovery unit of RTO's instead of ceramic saddles.

3) As filtrate substrate, ceramic honeycomb materials are generally utilized in food processing, water treatment, environmental industry, metallurgical industry etc.

3.Shapes and sizes

1)The shapes include as follows: round, square, triangular, sector, or to be customized etc.

2) The size include below: standard type 150mm x 150mm x 300mm, 100mm x 100mm x 100mm, 100mm x 100mm x 150mm, other size can be manufactured according to customers' requirements.

4. Types

Ceramic Honeycomb Catalytic Converter

Infrared Honeycomb Ceramic Plate

Ceramic Honeycomb Filter

Heat Transfer Media for RTO

Catalyst Support Monolith

Honeycomb Ceramic

5.Physical property of the environmental protecting Honey comb ceramics

Size
mm

D*H

mm×mm

Specific area
m²/m³

void volume %

m³/m³

MPa/m

mm/s(ks/m)

Hardness

(Mohs)

Φ6-150

6-150--150-50

1200-605

61-97

0.5-150

1-5

3-1.6

4.7-9.7

6.5

6. Chemical Composition of the environmental protecting Honey comb ceramics

Chemical composition	Content	Chemical composition	Content
Al₂O₃	20-85	Acid resistance %	≥99.8%
SiO₂+Al₂O₃	92	Alkali resistance %	≥86%
Fe₂O₃	<0.8	Refractoriness °C	≥1200°C
Out porous ratio	7.0-10%	Thermal stability	250-20°C No crack after three times