MF-F1632-4T Reciprocation Horizontal Flat Glass tempering furnace

High temperature glass melting furnace

Technical Performance

The performance of the product described in the following text conforms to that made of the high-quality float glass specified by national standards in GB11614-1999Float Glass.

Note: (1) The thickness of glass should be ≥4mm

(2) Four-side edges of the glass should be ground by diamond wheel until being beveled. No hole or chamfers are allowed.

1. Maximum area of glass sheets array: 4 - 19mm 1300 × 3050mm
2. Minimum size of glass for processing: 300 × 300mm
3. Maximum size of individual glass sheet for processing:

4mm 900mm×2500mm

5mm 1200mm×2500mm

6-19mm 1600mm×3200mm

4.Thickness of glass for processing: 4 - 19 mm

5.Maximum area of glass for processing: 4.6m*m per tempering cycle

4.9m*m per glass sheet

Clearance of glass sheets array: longitudinal ≥50mm; transverse ≥20mm

Production Rate: high-quality float flat glass specified by GB11614-1999, four-side edges ground. No holes or chamfer are allowed.

Thickness 4 5 6 8 10 12 15 19

No. of tempering

Cycle per hour 18 15 13 10 7 5 3 2

Note: The productivity may be reduced by 10-30% in the following cases:

1. When the length of an individual piece of glass exceeds 3050mm
2. For low-E glass
3. Yield Rate: 97% (for high-quality float flat glass specified by GB11614-1999, with four-side edges ground, and no holes nor chamfers)
4. Glass Varieties to be Produced: Ordinary glass, pattern glass, reflective glass, color glazed glass and coated Low-E (Radiance Value: e≥0.06) glass

The Samples